OK AristoRod™ 69是一种适合要求具有低温冲击韧性高强度钢GMAW焊接的0.3Cr-1.4Ni-0.25Mo合金化实芯焊丝。OK AristoRod™ 13.29经过伊萨独有的先进表面特性(ASC)技术处理，其可将MAG焊接操作提升到全新高度，并且在机器人和自动化焊接中具有全方位的高效性。其特性包括优良的引弧性能；无故障高速送丝和远距离送丝；较高焊接电流下电弧极其稳定；飞溅少；较低烟尘排放；导电嘴磨损少且焊丝腐蚀防护得到改善。
Typical Tensile Properties
| AWS 80Ar/20CO2 (M21) As welded |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 17 % | 805 MPa | 715 MPa | - | - |
| EN 80Ar/20CO2 (M21) As welded |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 19 % | 800 MPa | 730 MPa | - | - |
| EN 80Ar/20CO2 (M21) Stress relieved |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| 20 % | 750 MPa | 690 MPa | 620 °C | 15 hr |
夏比V型缺口冲击性能| EN 80Ar/20CO2 (M21) As welded |
| Impact Value | Testing Temperature | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| 100 J | 20 °C | - | - |
| 73 J | -40 °C | - | - |
| EN 80Ar/20CO2 (M21) Stress relieved |
| Impact Value | Testing Temperature | Stress Relieved Testing Temp | Stress Relieved Testing Time |
| 130 J | 20 °C | 620 °C | 15 hr |
| 60 J | -20 °C | 620 °C | 15 hr |
| 60 J | -30 °C | 620 °C | 15 hr |
焊缝金属分析| Mn |
| Mn | Mo | C | Si | Ni | Cr |
| 1.54 % | - | - | - | - | - |
| Mo |
| Mn | Mo | C | Si | Ni | Cr |
| - | 0.24 % | - | - | - | - |
| C |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | 0.089 % | - | - | - |
| Si |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | 0.53 % | - | - |
| Ni |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | 1.23 % | - |
| Cr |
| Mn | Mo | C | Si | Ni | Cr |
| - | - | - | - | - | 0.26 % |
熔敷数据| 安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 80-280 A | 1-5,4 kg/h | 18-28 V | 0.8 mm | 2,7-14,7 m/min |
| 80-280 A | 1-5,4 kg/h | 18-28 V | 0.9 mm | 2,7-14,7 m/min |
| 80-280 A | 1-5,4 kg/h | 18-28 V | 1.0 mm | 2,7-14,7 m/min |
| 120-350 A | 1,5-6,6 kg/h | 20-33 V | 1.2 mm | 2,7-12,4 m/min |
| 225-480 A | 3,3-0 kg/h | 26-38 V | 1.6 mm | 3,1-8,1 m/min |