适用于焊接21% Cr-1% Ni或23% Cr-4% Ni型奥氏体-铁素体不锈钢的实芯抗腐蚀双相焊丝。OK Autrod 2307经过Ni的超合金化处理，可确保焊缝金属中适当的铁素体平衡。 低镍双相型焊丝可用于土木工程、储罐、容器等的焊接。此类钢材一般具有中等抗腐蚀性和优良的强度性能。 焊接方式与普通奥氏体钢相同，但应避免电流过高，并且层间温度最大不超过150°C。
Typical Tensile Properties
| As welded |
| Elongation | Tensile Strength | Yield Strength |
| 32 % | 730 MPa | 560 MPa |
夏比V型缺口冲击性能| As welded |
| Impact Value | Testing Temperature |
| 160 J | 20 °C |
| 60 J | -60 °C |
焊缝金属分析| Mn |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| 1.4 % | - | - | - | - | - | - | - |
| Mo |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | 3.20 % | - | - | - | - | - | - |
| Cu |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | - | 0.2 % | - | - | - | - | - |
| C |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | - | - | 0.01 % | - | - | - | - |
| Si |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | - | - | - | 0.5 % | - | - | - |
| Ni |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | - | - | - | - | 7.1 % | - | - |
| Cr |
| Mn | Mo | Cu | C | Si | Ni | N | Cr |
| - | - | - | - | - | - | - | 23.2 % |
熔敷数据| 安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 80-190 A | 1,1-3,1 kg/h | 16-24 V | 1.0 mm | 2,9-8,4 m/min |
| 180-280 A | 2,6-4,5 kg/h | 20-28 V | 1.2 mm | 4,9-8,5 m/min |