A continuous solid Ni-Cr-Mo electrode for welding of high alloyed Ni-base materials, 9% Ni steel and super austenitic steels of type 20Cr-25Ni with 4-6% Mo. Can also be used for welding carbon steel to Ni base steel. The weld metal has a very good toughness and is corrosion resistant over a wide range of applications in oxidising and reducing media.
Typical Tensile Properties
| As welded |
| Elongation | Tensile Strength | Yield Strength |
| 40 % | 750 MPa | 500 MPa |
| 42 % | 700 MPa | 500 MPa |
夏比V型缺口冲击性能| As welded |
| Impact Value | Testing Temperature |
| 120 J | -110 °C |
焊缝金属分析| Mn |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| 0.2 % | - | - | - | - | - | - | - |
| Mo |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | 16.0 % | - | - | - | - | - | - |
| C |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | 0.01 % | - | - | - | - | - |
| Si |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | - | 0.1 % | - | - | - | - |
| Ni |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | - | - | 61.0 % | - | - | - |
| Al |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | - | - | - | 0.3 % | - | - |
| Cr |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | - | - | - | - | 23.0 % | - |
| Fe |
| Mn | Mo | C | Si | Ni | Al | Cr | Fe |
| - | - | - | - | - | - | - | 1.0 % |
熔敷数据| 安培 | 熔敷率 | 电压 V | 直径 | 送丝速度 |
| 100-200 A | 2,5-5,5 kg/h | 21-27 V | 1.0 mm | 6-13 m/min |
| 160-280 A | 3,6-6 kg/h | 24-30 V | 1.2 mm | 6-10 m/min |
| 200-350 A | 4,3-8,6 kg/h | 25-32 V | 1.6 mm | 4-8 m/min
|