Stanyl® TE248F6Polyamide 46
Product Description:
30% Glass Reinforced, Heat Stabilized, UV Stabilized
| General | |
Material Status | |
Literature 1 | |
UL Yellow Card 2 | |
Search for UL Yellow Card | |
Availability | |
Filler / Reinforcement | - Glass Fiber, 30% Filler by Weight
|
Additive | |
Features | |
Forms | |
| Physical | Dry | Conditioned | Unit | Test Method |
Density | 1.41 | -- | g/cm³ | ISO 1183 |
Molding Shrinkage | | | | ISO 294-4 |
Across Flow | 1.3 | -- | % | |
Flow | 0.50 | -- | % | |
Water Absorption (Equilibrium, 23°C, 50% RH) | 2.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | | | | ISO 527-2 |
-- | 10000 | 6000 | MPa | |
120°C | 5500 | -- | MPa | |
160°C | 5000 | -- | MPa | |
Tensile Stress | | | | ISO 527-2 |
Break | 210 | 115 | MPa | |
Break, 120°C | 110 | -- | MPa | |
Break, 160°C | 100 | -- | MPa | |
Tensile Strain | | | | ISO 527-2 |
Break | 4.0 | 7.0 | % | |
Break, 120°C | 7.5 | -- | % | |
Break, 160°C | 7.5 | -- | % | |
| Impact | Dry | Conditioned | Unit | Test Method |
Notched Izod Impact Strength (23°C) | 12 | 19 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | | | | |
0.45 MPa, Unannealed | 290 | -- | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 290 | -- | °C | ISO 75-2/A |
Melting Temperature 3 | 295 | -- | °C | ISO 11357-3 |
CLTE | | | | ISO 11359-2 |
Flow | 2.5E-5 | -- | cm/cm/°C | |
Transverse | 6.0E-5 | -- | cm/cm/°C | |
RTI Elec (0.75 mm) | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
Electric Strength | 35 | 25 | kV/mm | IEC 60243-1 |
Relative Permittivity | | | | IEC 60250 |
100 Hz | 4.40 | 12.0 | | |
1 MHz | 4.00 | 4.60 | | |
1.00 GHz | 3.60 | -- | | |
Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
Flammability Classification | | | | IEC 60695-11-10, -20 |
0.75 mm | HB | -- | | |
1.5 mm | HB |