BrazeTec h 86 Paste
TD TM-BT 0905 E.00
Inhalt
Standard
DIN EN 1045 FH10
Based on boron compounds, fluorides
Technical Data
Working temperature range approx. 550 - 850 °C
Colour white
Density approx. 1.8 g/cm³ (20 °C)
Viscosity 120 - 240 dPa s (Haake Viscotester 02, Sp.2, 20 ±2 °C)
Flux residues corrosive, water-soluble
Shelf life min. 6 months, but only in the original sealed container
at storage temperatures between +5 to +30 °C.
avoid rapid changes in temperature.
Packaging
Standard 3.0 ; 10 kg Technical Data Sheet
BrazeTec h 280 Paste
| Standard | FH10 |
| Based on | boron compounds, fluorides, organic binder |
| Technical Data | approx. 520 - 850 °C |
Colour white
Density approx. 1.3 g/cm³ (20 °C)
Viscosity 450 - 550 dPa s (Haake
Viscotester 02, Sp.2, 20 ±2 °C)
Cleaning agent BrazeTec Cleaning Agent P
Flux residues corrosive, water-soluble
Shelf life min. 6 months, but only in the
original sealed container
at storage temperatures
between +5 to +30 °C.
avoid rapid changes in
temperature.
stir well before use.
Packaging
|
Standard |
1.5; 20 kg |
|
Applications |
|
|
BrazeTec h 280 is a dosable flux paste which can be applied via a suitable applicator at the mouth of |
|
|
the gap. Normally it is used in mechanised brazing procedures. The paste should be homogenised |
|
|
prior to loading in the tank of the applicator. |
|
|
The flux paste is suitable for brazing any steels, copper and copper alloys as well as nickel and nickel |
|
|
alloys. |
|
|
BrazeTec h 280 can be used for all flame and particular for induction brazing procedures. During |
|
|
brazing the organic binder must burn out completely. |
|
|
Typical applications are found e.g. in the automotive and electrical industry. |