PA66是什么材料的概述:因为PA66具有优异的机械性能所以被广泛应用于汽车配件上面 。40年代末期美国DoPont公司实现PA66工业化生产,目前世界上尼龙树脂按结构分大约有20多种， 商品牌号达800馀种。以尼龙大分子中重复单元的碳原子数目来确定其产品名称，通式可写尼龙或PA。有PA6、PA66、PA11、PA12、PA610、PA612、PA1010、PA46、PA6T、PA9T等。其中以品种PA6、PA66为主，二者约占PA工程塑料总量的92%左右。
| 密度 | 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 |
| 填料含量 | 30 % | 30 % | DAM |
| Water Absorption | 2.0 % @Thickness 1.00 mm, Temperature 23.0 °C | 2.0 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to |
| 6.9 % @Thickness 1.00 mm, Temperature 23.0 °C | 6.9 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |
| 线性成型收缩率,Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 线性成型收缩率，横向 | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | DAM; ISO 294-4 |
| 抗张强度(断裂) | 130 MPa @Temperature 23.0 °C | 18900 psi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 195 MPa @Temperature 23.0 °C | 28300 psi @Temperature 73.4 °F | DAM; ISO 527 | |
| 伸长率 (断裂) | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ISO 527 |
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |
| 拉伸模量 | 7.20 GPa @Temperature 23.0 °C | 1040 ksi @Temperature 73.4 °F | 50%RH; ISO 527 |
| 9.80 GPa @Temperature 23.0 °C | 1420 ksi @Temperature 73.4 °F | DAM; ISO 527 | |
| 悬壁梁缺口冲击强度 | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A |
| 14.0 kJ/m² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |
| 简支梁无缺口冲击强度 | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU |
| 8.00 J/cm² @Temperature 23.0 °C | 38.1 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |
| 9.30 J/cm² @Temperature 23.0 °C | 44.3 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |
| 简支梁缺口冲击强度 | 1.30 J/cm² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA |
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA |
| 体积电阻率 | 1.00e+13 ohm-cm @Temperature 23.0 °C | 1.00e+13 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 |
| 表面电阻 | 1.00e+12 ohm @Temperature 23.0 °C | 1.00e+12 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 |
| 耗散因数 | 0.016 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.016 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 |
| 0.016 @Frequency 100 Hz, Temperature 23.0 °C | 0.016 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C | >= 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A |
| 600 V @Thickness 3.00 mm, Temperature 23.0 °C | 600 V @Thickness 0.118 in, Temperature 73.4 °F | DAM; UL 746A |
| 熔融温度 | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 载荷下热变形温度(1.8 MPa) | 253 °C | 487 °F | DAM; ISO 75-1/-2 |
| 玻璃化转变温度，Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 |
| UL RTI | 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B |
| 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | DAM; UL 746B | |
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B | |
| UL RTI，机械冲击 | 120 °C @Thickness 0.710 mm | 248 °F @Thickness 0.0280 in | DAM; UL 746B |
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | |
| UL RTI，机械无冲击 | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | DAM; UL 746B |
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | DAM; UL 746B | |
| 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | DAM; UL 746B | |
| 可燃性(UL94) | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; UL94 | |
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |
| HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | DAM; IEC 60695-11-10 | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |
| 极限氧指数 | 24 % | 24 % | DAM; ISO 4589-1/-2 |
| 加工（熔体）温度 | 295 °C | 563 °F | DAM; Optimum |
| 285 - 305 °C | 545 - 581 °F | DAM | |
| 模具温度 | 70.0 - 120 °C | 158 - 248 °F | DAM |
| 100 °C | 212 °F | DAM; optimum | |
| 干燥温度 | 80.0 °C | 176 °F | DAM |
| 干燥时间 | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| 水分含量 | <= 0.20 % | <= 0.20 % | DAM |
| 外观 | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| 特性 | Chemical Resistance, Good | DAM |
| Creep Resistance, Good | DAM | |
| Fatigue Resistant | DAM | |
| Fuel Resistant | DAM | |
| General Purpose | DAM | |
| Grease Resistant | DAM | |
| Lubricated | DAM | |
| Oil Resistant | DAM | |
| Stiffness, High | DAM | |
| Strength, High | DAM | |
| Filler | Glass fiber reinforcement | DAM |
| 形式 | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| 部件标识代码 | >PA66-GF30< | ISO 11469; DAM |
| Polymer Family | Polyamide | DAM |
| Polymer Type | PA66 | DAM |
| 加工方法 | Injection Molding | DAM |
| 产品分类 | Glass Reinforced Resins | DAM |
| Glass Reinforced Resins | DAM | |
| Region Available - Global | Yes | DAM |
| 树脂识别 | PA66-GF30 | ISO 1043; DAM |
| 符合RoHS指令 | Contact Manufacturer | DAM |
| 用途 | Appliance Components | DAM |
| Automotive Applications | DAM | |
| Electrical/Electronic Applications | DAM | |
| Industrial Applications | DAM |
 |
PA66材料特性（二）1.官能基-NHCO-有強烈的吸水性质2.耐酸性差3.因吸湿性高，故长期尺寸精密度下降以及物性电气性质受影响