PBT S600F10美国杜邦产品说明--Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection Molding

　　PBT S600F10美国杜邦--Physical performance rating unit system test method

　　Density: 1.30 g / cm? ISO 1183

　　Melt flow rate (melt flow rate) (250 ° C / 2.16 kg) 10 g / 10 min ISO 1133

　　Shrinkage: ISO 294-4

　　Vertical flow direction 1.6% ISO 294-4

　　Flow direction 1.7% ISO 294-4

　　Water absorption ISO 62

　　23°C, 24 hr, 2.00 mm 0.50 % ISO 62

　　Balanced, 23 ° C, 2.00 mm, 50% RH 0.20% ISO 62

　　Mechanical properties rating unit system test method

　　Tensile modulus 2600 MPa ISO 527-2

　　Tensile stress (yield) 57.0 MPa ISO 527-2

　　Tensile strain (yield) 4.0% ISO 527-2

　　Nominal tensile breaking strain > 50% ISO 527-2

　　Tensile creep modulus ISO 899-1

　　1 hr 2600 MPa ISO 899-1

　　1000 hr 1800 MPa ISO 899-1

　　Bending modulus 2300 MPa ISO 178

　　Bending stress 85.0 MPa ISO 178