英国进口MWA铸铁焊条Mac Cast E407|ENiFe-CI|铸铁焊接|压力容器焊接

High strength machinable electrode for joining and building up on cast irons. Low amperage, smooth arc, minimum spatter and high resistance to cracking. For the repair of grey, S.G., nodular or ductile irons where higher strength is required. Also suitable for joining cast iron to mild steel (in conjunction with Mac Groove 71), pressure vessels, etc.

高强度可加工镍铁焊条，用于铸铁的连接和堆焊。电流低，电弧平滑，飞溅小，抗裂性高。用于需要更高强度的灰铸铁、球墨铸铁的修复。也适用于连接铸铁和低碳钢（与Mac Groove E71切割焊条一起使用）、压力容器等。有对应MIG焊丝可供选择。

Typical All Weld Metal Mechanical Properties（As Welded） 

典型全焊缝金属机械性能（焊态）：

Ultimate Tensile Strength 抗拉强度： 448 N/mm²

Elongation 延伸率：                              20%

Hardness 硬度：                                   180 HB

Sizes Available and Recommended Amperages

尺寸Φ/电流：

Current电流：AC/DC (+)

Related Specification参考标准：AWS A5.15 ENiFe-CI

Storage储存：Electrodes should be stored in dry conditions. Should the electrodes

become damp, re-dry for one hour at 150°C before use. 焊条应储存在干燥环境中。如果焊条受潮，应在150°C下重新干燥1小时后再使用。  

使用注意事项：

根据操作者的熟练程度，如采用上限焊接电流施焊及焊接的位置不同，相应提高焊接速度或采用短断弧焊来减少焊接热输入量避免焊缝白口组织。

如有可能，清洁焊接区域。去除表皮和所有锐边。

坡口接头形成“U”形槽。

焊孔必须与所有裂纹的两端成直角，以防止焊接过程中扩展。

使用低电流并保持短电弧。应使用短线状焊道或窄编织焊道，以防止过热。

采用直流焊机时根据熔敷情况改变正负极。

断开电弧时，始终填充弧坑，并将焊条拉回到焊缝沉积物上。

趁热敲击将有助于降低应力。重新引弧时，电弧从先前沉积的焊缝金属开始，而不是从母材开始。

让零件慢慢冷却。