东莞东利塑胶销售 毛总15807693310---东利15322412218
QQ:1574559134
ARLEN A315
PA6T
三井化学 (Mitsui Chemicals)
产品描述
ARLEN™ A315 by Mitsui Chemicals is a modified polyamide 6T reinforced with 15% glass fiber. Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity even in a high-temperature atmosphere such as the inside of an engine room. Is suitable for processing by injection molding. ARLEN™ A315 is used in mechanical and structural applications including under the hood parts such as cooling system parts, cylinder head covers, thermostat cases, hydraulic system pistons and oil pump housings. Recommended for light-load tribological application parts of office automation equipment. Complies with UL 94 HB flame rating.
Features:
Possesses high dimensional stability, high melting point (320°C), minimum water absorption and high glass transition point (125°C). Exhibits good chemical and heat resistance. Offers high rigidity
Applications:
Mechanical and structural parts
基本信息
| 原厂资料 | ||||
| 产品特性 | 高刚性耐热尺寸稳定耐化学性填充增强 | |||
| 增强填充 | 15% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.3 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5 % | ASTM D 955 | 2mm |
横向(Across Flow) | 0.6 % | ASTM D 955 | 2mm |
吸水率 | 2.5 % | ASTM D570 | 24 hr, 100°C, 2mm |
吸水率 | 0.4 % | ASTM D570 | 24 hr, 23°C, 2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 120 Mpa | ASTM D 638 | dry |
- | 110 Mpa | ASTM D 638 | moist |
拉伸延伸率 | |||
- | 3 % | ASTM D 638 | dry |
- | 3 % | ASTM D 638 | moist |
弯曲强度 | |||
- | 190 Mpa | ASTM D790 | dry |
- | 170 Mpa | ASTM D790 | moist |
弯曲模量 | 6000 Mpa | ASTM D790 | dry |
弯曲模量 | 5500 Mpa | ASTM D790 | moist |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 50 J/m | ASTM D256 | dry |
23℃ (73℉) | 70 J/m | ASTM D256 | moist |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 105 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 290 °C | ASTM D648 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 34 E-6/°C | ASTM D 696 | |
横向(Across Flow) | 55 E-6/°C | ASTM D 696 | |
熔融温度(Tm) | 330 °C | Internal | |
玻璃化温度(Tg) | 125 °C | Internal | |
ARLEN C215 日本三井 尼龙6T
ARLEN C240 日本三井 尼龙6T
ARLEN C230 日本三井 尼龙6T
ARLEN A335 日本三井 尼龙6T
ARLEN AE2230 日本三井 尼龙6T
ARLEN AE4200N 日本三井 尼龙6T
ARLEN C240N 日本三井 尼龙6T
ARLEN AE4200 日本三井 尼龙6T
ARLEN CH245NK 日本三井 尼龙6T
ARLEN E430N 日本三井 尼龙6T
ARLEN C430N 日本三井 尼龙6T
ARLEN C230N 日本三井 尼龙6T
ARLEN E630N 日本三井 尼龙6T
ARLEN E440NK 日本三井 尼龙6T 玻纤增强40 耐化学性 吸水低 阻燃性 电气电子应用领域 开关 连接器
ARLEN G335 日本三井 尼龙6T
ARLEN A350 日本三井 尼龙6T
ARLEN A315 日本三井 尼龙6T
PA6T全称聚对苯二甲酰己二胺，ARLEN为日本三井化学公司(MitsuiChemicals,Inc)所开发出的一种耐热性尼龙6T/66，是一种PA6TPA6T与PA66共聚的产物。
其电子零件用的PA6T/66为一种基于对苯二甲酸，己二酸及己二胺的改性尼龙6T，其熔点高达310℃。 PA6T/66的主要特性为高温刚性，尺寸安定性以及耐化学品性。 特性使PA6T在许多领域包括汽车零件，机械零件以及电气/电子零件上有广泛的应用。以下用PA6T泛指PA6T/66。
三井化学公司配制了各种不同等级的PA6T。 整体来说，PA6T的主要特性如下：
1. 耐焊接性
PA6T具有很高的熔点(310℃)，其热变形温度也很高(约290℃)，因此可显现耐焊接性(reflow solderability)。耐焊接性使PA6T特别适用于表面黏着技术(SMT)用电子连接器。
2.高温刚性
PA6T在高温下仍可维持相当高的模数，譬如说在120℃时的模量为23℃时模量的55%。也就是说PA6T在广泛温度范围间可维持稳定而且刚性。
3.耐化学品性
4. 吸水率低
对于尼龙树脂而言，PA6T的吸水率相当低，仅为尼龙66的1/4至1/3。因此，PA6T因吸水所造成的物性变化相对较小。
5.尺寸稳定性
PA6T的吸水率相当低，因吸水而造成的尺寸变化相当小。 PA6T的热膨胀系数相当稳定，在高温范围中仍然维持在相当低的水准，因此，对温度变化的尺寸稳定性良好。 此外，PA6T因成型过程所造成翘曲很小。也就是说PA6T具有尺寸稳定性。
6. 流动性
PA6T具有良好的熔融流动性，很容易以射出成型来加工。 此外，PA6T还具有薄壁成型性，使其适于小零件的加工成型。
7. 成型时不易起毛边
PA6T也拥有尼龙所固有的一个特性，在射出成型时不易起毛边。