PC L-1250Y 日本帝人化成公司 物性数据①原料描述部分规格级别：---外观颜色：---用途概述：对流动性要求较高的薄壁制品、电器、电子元件、机械零件、劳保、医疗用品、照明器具及灯罩、餐具、容器。备注说明：特性：最适宜于采用注坯吹塑成型
②原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率24hr，in 23℃ASTM D-5700.20%物理性能比重---ASTM D-7921.20---透光率厚度3mmASTM D-100388%折射率---ASTM D-5421.585---阻燃性厚度1.47mmUL 9494V-2---阻燃性厚度3.05mmUL 9494V-2---机械性能拉伸强度屈服点断裂点---ASTM D-638ASTM D-63861(620)81(830)Mpa(kgf/cm2)Mpa(kgf/cm2)拉伸模量---ASTM D-6382120(21600)Mpa(kgf/cm2)拉伸率屈服点断裂点---ASTM D-638ASTM D-6386140---弯曲强度---ASTM D-79090(915)Mpa(kgf/cm2)弯曲模量---ASTM D-7902230(22700)Mpa(kgf/cm2)压缩强度---ASTM D-69576(770)Mpa(kgf/cm2)耐冲击强度值艾氏、带缺口厚度3.2mmASTM D-256880(90)j/m(kgf.cm/cm)耐冲击强度值艾氏、带缺口厚度6.4mmASTM D-256140(14)j/m(kgf.cm/cm)洛氏硬度---ASTM D-78577M标度电气性能耐导电径迹性（CTI）---IEC 112300V绝缘破坏强度快速加压值厚度1.6mmASTM D-14930KV/mm体积电阻率---ASTM D-25731016Ω.cm介电率60HzASTM D-1502.95---介电率106HzASTM D-1502.9---介电正切60HzASTM D-1500.0004---介电正切106HzASTM D-1500.009---耐电弧性---ASTM D-495110secc加工性能成型收缩率流动方向垂直方向---ASTM D-955ASTM D-9550.5～0.70.5～0.7%%热 性 能负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTM D-648143°C负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTM D-648143°C线膨胀系数流动方向垂直方向---ASTM D-696ASTM D-6967710-5cm/cm/℃10-5cm/cm/℃温度指数电学式冲击式非冲击式厚度1.47mm厚度1.47mm厚度1.47mmUL 746BUL 746BUL 746B125115125°C°C°C