产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜50%RH,1.2｜- | % |
| 吸水率 | 饱和(23℃) | ASTM D-570 | DAM｜50%RH,8.5｜- | % |
| 比重 | | ASTM D-792 | DAM｜50%RH,1.14｜1.14 |
| 泰伯磨耗量 | cs-17 Wheel 1000g | | DAM｜50%RH,-｜7 | mg/1000 cycles |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜50%RH,53｜112 | j/m |
| 洛氏硬度M | | ASTM D-785 | DAM｜50%RH,M79｜M59 |
| 硬度计硬度 | | ASTM D-676 | DAM｜50%RH,89｜82 |
| 洛氏硬度R | | ASTM D-785 | DAM｜50%RH,R121｜R108 |
| 屈服强度 | 23℃ | | DAM｜50%RH,82.7｜58.6 | MPa |
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜50%RH,82.7｜77.2 | MPa |
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜50%RH,2827｜1207 | MPa |
| 拉伸冲击强度 | 短试样23℃ | ASTM D-1822 | DAM｜50%RH,157｜231 | KJ/m2 |
| 1%形变时的压应力 | | ASTM D-695 | DAM｜50%RH,33.8｜- | MPa |
| 剪切强度 | 23℃ | ASTM D-732 | DAM｜50%RH,66.2｜- | MPa |
| 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜50%RH,60｜≥300 | % |
| 屈服伸长率 | | ASTM D-638 | DAM｜50%RH,5｜25 | % |
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜50%RH,504｜1470 | KJ/m2 |
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜50%RH,3.6｜4.6 |
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜50%RH,0.01｜0.2 |
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜50%RH,3.9｜7.0 |
| 耗散因数 | 106Hz(cps) | ASTM D-150 | DAM｜50%RH,0.02｜0.1 |
| 耗散因数 | 103Hz(cps) | ASTM D-150 | DAM｜50%RH,0.02｜0.2 |
| 体积电阻率 | | ASTM D-257 | DAM｜50%RH,10,15,｜10,13 | Ω.cm |
| 介电常数 | 100Hz(cps) | ASTM D-150 | DAM｜50%RH,4.0｜8.0 |
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜50%RH,1.4｜- | % |
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜50%RH,90｜- | ℃ |
| 熔点结晶 | | ASTM D-2177 | DAM｜50%RH,270｜- | ℃ |
| UL可燃性导级 | | UL 94 | DAM｜50%RH,94｜V-2 |
| 脆化温度 | | ASTM D-746 | DAM｜50%RH,-80｜-65 | ℃ |
| 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜50%RH,235｜- | ℃ |
| 导热系数 | | | DAM｜50%RH,0.25｜- | w/mk |
| 线性热膨胀系数 | | ASTM D-696 | DAM｜50%RH,7×10,-5,｜- | m/m/℃ |
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜50%RH,255｜255 | ℃ |
| 需氧指数 | | ASTM D-2863 | DAM｜50%RH,28｜31 | % |