Tensile Stress, yld, Type I, 50 mm/min

710

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

610

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

5.4

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

88.1

%

ASTM D 638

Tensile Modulus, 5 mm/min

24900

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1150

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

26300

kgf/cm²

ASTM D 790

Izod Impact, notched, 23°C

7

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

7

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

734

cm-kgf

ASTM D 3763

Vicat Softening Temp, Rate B/50

132

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

127

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

116

°C

ASTM D 648

CTE, -40°C to 40°C, flow

6.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.5E-05

1/°C

ASTM E 831

Vicat Softening Temp, Rate B/120

135

°C

ISO 306

Specific Gravity

1.2

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.96

%

SABIC Method

Melt Flow Rate, 300°C/1.2 kgf

10.5

g/10 min

ASTM D 1238

Density

1.2

g/cm³

ISO 1183

Drying Temperature

75 - 90

°C

Drying Time

2 - 4

hrs

Minimum Moisture Content

0.04

%

Melt Temperature

180 - 200

°C

Barrel - Zone 1 Temperature

165

°C

Barrel - Zone 2 Temperature

170

°C

Barrel - Zone 3 Temperature

175

°C

Barrel - Zone 4 Temperature

180

°C

Roll Stack Temperature - Top

175 - 180

°C

Roll Stack Temperature - Middle

175 - 180

°C

Roll Stack Temperature - Bottom

175 - 180

°C