LNP* Thermocomp* Compound
Thermocomp 玻纤/碳纤维增强复合材料具有出色的机械性能和热学性能，包括优异的耐高温、耐疲劳、耐蠕变、耐冲击和耐受化学药品的特性。Thermotuf* 复合材料经过抗冲击改性，韧性大大提高。Thermocomp系列还包括高比重(HSG)复合材料、可熔化加工的含氟聚合物复合材料和用于薄壁模塑的极佳工艺性 （EP） 复合材料，Thermocomp系列中的产品通常用于汽车功能部件、商用机器、电子/电气元件、消费
LNP* Thermocomp* Compound DF002H |
| | |
| | | Americas: COMMERCIAL |
| Also known as:LNP* Thermocomp* Compound DF-1002 HC |
| Product reorder name:DF002H |
LNP THERMOCOMP* DF002H is a compound based on Polycarbonate resin containing Glass Fiber. Characteristic of this grade is Healthcare. |
Property |
| TYPICAL PROPERTIES(1) | ||||
MECHANICAL | Value | Unit | Standard | |
Tensile Stress, yld, Type I, 5 mm/min | 820 | kgf/cm² | ASTM D 638 | |
Tensile Stress, brk, Type I, 5 mm/min | 760 | kgf/cm² | ASTM D 638 | |
Tensile Strain, yld, Type I, 5 mm/min | 3.9 | % | ASTM D 638 | |
Tensile Strain, brk, Type I, 5 mm/min | 5.6 | % | ASTM D 638 | |
Tensile Modulus, 50 mm/min | 43300 | kgf/cm² | ASTM D 638 | |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1400 | kgf/cm² | ASTM D 790 | |
Flexural Modulus, 1.3 mm/min, 50 mm span | 41900 | kgf/cm² | ASTM D 790 | |
Tensile Stress, yield, 5 mm/min | 80 | MPa | ISO 527 | |
Tensile Stress, break, 5 mm/min | 74 | MPa | ISO 527 | |
Tensile Strain, yield, 5 mm/min | 3.8 | % | ISO 527 | |
Tensile Strain, break, 5 mm/min | 5.7 | % | ISO 527 | |
Tensile Modulus, 1 mm/min | 4170 | MPa | ISO 527 | |
Flexural Modulus, 2 mm/min | 3950 | MPa | ISO 178 | |
IMPACT | Value | Unit | Standard | |
Izod Impact, unnotched, 23°C | 90 | cm-kgf/cm | ASTM D 4812 | |
Izod Impact, notched, 23°C | 8 | cm-kgf/cm | ASTM D 256 | |
Multiaxial Impact | 107 | cm-kgf | ISO 6603 | |
Instrumented Impact Total Energy, 23°C | 187 | cm-kgf | ASTM D 3763 | |
Izod Impact, unnotched 80*10*4 +23°C | 54 | kJ/m² | ISO 180/1U | |
Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A | |
THERMAL | Value | Unit | Standard | |
HDT, 0.45 MPa, 3.2 mm, unannealed | 146 | °C | ASTM D 648 | |
HDT, 1.82 MPa, 3.2mm, unannealed | 141 | °C | ASTM D 648 | |
CTE, -30°C to 30°C, flow | 4.55E+01 | 1/°C | ASTM D 696 | |
CTE, -30°C to 30°C, xflow | 5.3E+01 | 1/°C | ASTM D 696 | |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 54 | °C | ISO 75/Bf | |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 8 | °C | ISO 75/Af | |
PHYSICAL | Value | Unit | Standard | |
Density | 1.29 | g/cm³ | ASTM D 792 | |
Moisture Absorption, 50% RH, 24 hrs | 0.14 | % | ASTM D 570 | |
Mold Shrinkage, flow, 24 hrs (5) | 0.4 - 0.6 | % | ASTM D 955 | |
Mold Shrinkage, xflow, 24 hrs (5) | 0.6 - 0.8 | % | ASTM D 955 | |
Density | 1.29 | g/cm³ | ISO 1183 | |
Moisture Absorption (23°C / 50% RH) | 0.2 | % | ISO 62 | |
Source GMD, last updated:2011/09/21 |
Processing |
| Parameter | ||
Injection Molding | Value | Unit |
Drying Temperature | 120 | °C |
Drying Time | 4 | hrs |
Maximum Moisture Content | 0.02 | % |
Melt Temperature | 305 - 325 | °C |
Front - Zone 3 Temperature | 320 - 330 | °C |
Middle - Zone 2 Temperature | 310 - 320 | °C |
Rear - Zone 1 Temperature | 295 - 305 | °C |
Mold Temperature | 80 - 110 | °C |
Back Pressure | 0.2 - 0.3 | MPa |
Screw Speed | 30 - 60 | rpm |
专业从事沙伯基础LNP* Thermocomp PC工程塑料进出口业务的贸易型公司。不仅是专业的原料供应商，亦注重技术支持及全方位的解决方案，提供从材料鉴定、模具设计、成型加工等系列帮助，亦可为客户量身定制各特殊性能之材料，进而协助客户提高产品竟争力。同时为广大客户提供相关LNP* Thermocomp PC工程塑胶原料材质证明、UL证书及MSDS报告。