55crSi琴钢丝介绍介绍：

瑞和日标琴钢丝图片


琴钢丝是经铅浴淬火后冷拉而成，具有非常高的强度极限和弹性极限，是广泛应用的小弹簧材料。钢丝的质量、性能要求严格，除拉伸试验外，还需作扭转、腐蚀、锐碳等试验。按用途可分为制造各种重要弹簧、各种高应力和械弹簧及伐门弹簧所用的琴钢丝。

American standard: ASTM

Jean steel wire is the lead bath after a cold pull quenching, it has a very high intensity limit and elastic limit, it is widely applied to the small spring material. The quality of the steel wire, performance requirements strictly, in addition to the tensile test, will have to be twisted, corrosion, sharp carbon test and etc. ording to use can be pided into manufacturing various important spring, all kinds of high stress and gave the spring and cut the piano wire used valve spring.

　　用于制造琴弦、阀弹簧和高应力弹簧的钢丝。具有强度高，弹性、抗疲劳、抗蠕变和韧性好，表面光滑洁净，防锈能力强以及音乐性能优良等特点。钢丝用钢包括碳素钢和不锈钢。(见合金钢丝)碳素琴钢丝用高碳优质碳素结构钢和碳素工具钢制造。钢中硫、磷的含量均不得超过0.025%，铜的含量不得超过0.20%。琴钢丝的直径约在0.08～6mm之间。每盘钢丝应由一根钢丝组成，不允许有焊接接头存在。钢丝应具有规定的抗拉强度和扭转性能。用作阀弹簧的琴钢丝一面上的总脱碳层深度不得超过丝径的1%。钢丝表面不得有裂纹、折叠、结疤、拉裂、氧化铁皮和锈蚀、钢丝的表面状态有不抛光、抛光和镀层等类。镀层钢丝具有光亮、美观和耐磨蚀等特点。镀层材料有镉、锡和锌一镍合金等。为了保证琴钢丝的质量，对盘条的化学成分、内部组织的均匀性、非金属夹杂、气体含量、晶粒的均匀度、表面缺陷、脱碳层及不圆度等都有严格的要求。拉制成品前的热处理一般采用电接触加热的索氏体化处理，以保证钢丝通条性能均匀并提高加热速度、缩短加热时间，减少因加热而产生的氧化铁皮和脱碳层。热处理后线坯采用盐酸酸洗，以加快酸洗速度和使钢丝表面具有良好的表面质量。酸洗后对不镀层的钢丝可采用磷化涂层处理，对镀层钢丝则采用黄化或硼砂处理。成品拔程的总减面率和平均道次减面率(见面积减缩率)，对于干拉约为88%～92%和15%～17%；对于湿拉约为93%～96%和16%～18%。通常采用适当减少道次减面率和相应增加一些拉拔道次的拉拔工艺。对于弹簧用琴钢丝，平直度很重要，拉拔时要通过调整拉丝模模架的角度或矫直辊的位置，进行严格控制。