美国GE：ASA：XTWFR15(图)
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 30 | g/10min |
| 物理性能 | 比重 | | ASTM D-792 | 1.20 | g/cm3 |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.40-0.70 | % |
| 机械性能 | 拉伸模量 | | ASTM D-638 | 2220 | MPa |
| 拉伸屈服强度 | | ASTM D-638 | 46.0 | MPa |
| 拉伸断裂强度 | | ASTM D-638 | 34.0 | MPa |
| 拉伸屈服伸长率 | | ASTM D-638 | 2.7 | % |
| 拉伸断裂伸长率 | | ASTM D-638 | 11 | % |
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 2070 | MPa |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 64.0 | MPa |
| IZOD缺口冲击强度 | -30℃ | ASTM D-256 | 20.0 | J/m |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 70.0 | J/m |
| 电气性能 | 介电强度 | 0.800mm,in oil | ASTM D-148 | 41.0 | KV/mm |
| 介电强度 | 1.60mm,in oil | ASTM D-148 | 24.0 | KV/mm |
| 介电强度 | 3.20mm,in oil | ASTM D-148 | 18.0 | KV/mm |
| 介电常数 | 1000Hz | ASTM D-150 | 3.400 | |
| 介电常数 | 1E+6Hz | ASTM D-150 | 3.200 | |
| 介电损耗因数 | 1000Hz | ASTM D-150 | 0.0080 | |
| 介电损耗因数 | 1E+6Hz | ASTM D-150 | 0.029 | |
| 热性能 | 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 76.0 | ℃ |
| 维卡软化温度 | | ASTM D-1525 | 85.0 | ℃ |
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000098 | cm/cm/℃ |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000099 | cm/cm/℃ |
| 燃烧性 | 1.50mm | UL 94 | V-0 | |
| 燃烧性 | 3.00mm | UL 94 | 5VB | |