美国GE:ASA:CR5020(图)
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 基本性能 | 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 7.1 | g/10min |
| 物理性能 | 比重 | | ASTM D-792 | 1.06 | g/cm3 |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % |
| 机械性能 | 拉伸模量 | | ASTM D-638 | 2070 | MPa |
| 拉伸屈服强度 | | ASTM D-638 | 40.7 | MPa |
| 拉伸断裂强度 | | ASTM D-638 | 31.7 | MPa |
| 拉伸屈服伸长率 | | ASTM D-638 | 3.0 | % |
| 拉伸断裂伸长率 | | ASTM D-638 | 24 | % |
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 2140 | MPa |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 62.1 | MPa |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 320 | J/m |
| 洛氏硬度 | | ASTM D-785 | 95 | R scale |
| 热性能 | 热变形温度 | 0.45MPa,未退火,3.20mm | ASTM D-648 | 87.8 | ℃ |
| 热变形温度 | 1.80MPa,未退火,3.20mm | ASTM D-648 | 77.8 | ℃ |
| 维卡软化温度 | | ASTM D-1525 | 99.4 | ℃ |
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000086 | cm/cm/℃ |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ |
产品细节图