供应太空杯用PCTG TX1801 不含双酚A Tritan材料
深圳市百利丰塑胶原料有限公司
中国 东莞
产品属性
图文详情
品牌推荐
品牌/厂家
美国伊士曼
牌号
TX1801
类型
正牌料
用途级别
注射级
产地
美国
熔体流动速率
10g/10min
密度
1.18g/cm3
拉伸强度
52kg/cm2
弯曲强度
64kg/cm2
弯曲模量
1522kg/cm2
缺口冲击强度
842kg.cm/cm
断裂伸长率
140%
成型收缩率
0.6%
热变形温度
101℃
脆化温度
-40℃
维卡软化点
NULL°F
雾度
1%
透光率
89%
干燥温度
88℃
干燥时间
4-6hrs
模具温度
35-55℃
| Product Data Sheet Eastman Tritan™ Copolyester TX1801 Natural | ||||||||
| ||||||||
| Product Description | ||||||||
| Eastman Tritan™ Copolyester TX1801 is an amorphous copolyester specifically developed for use in blow molding applications. Eastman Tritan™ Copolyester TX1801 contains a mold release derived from vegetable based sources. Its most outstanding features are excellent toughness, hydrolytic stability, heat resistance, and chemical resistance. In addition, this new generation copolyester offers excellent appearance and clarity. Eastman Tritan™ Copolyester TX1801 may be used in repeated use food contact articles under United States Food and Drug Administration (FDA) regulations. | ||||||||
| Typical Properties (Preliminary) | ||||||||
| Propertya | Testb Method | Typical Value, Unitsc | ||||||
| General Properties | ||||||||
| Specific Gravity | D 792 | 1.18 | ||||||
| Mold Shrinkage | D 955 | 0.006 mm/mm (0.006 in./in.) | ||||||
| Mechanical Properties | ||||||||
| Tensile Stress @ Yield | D 638 | 45 MPa (6500 psi) | ||||||
| Tensile Stress @ Break | D 638 | 52 MPa (7600 psi) | ||||||
| Elongation @ Yield | D 638 | 7% | ||||||
| Elongation @ Break | D 638 | 139% | ||||||
| Tensile Modulus | D 638 | 1609 MPa (2.3x105 psi) | ||||||
| Flexural Modulus | D 790 | 1522 MPa (2.2x105 psi) | ||||||
| Flexural Yield Strength | D 790 | 64 MPa (9300 psi) | ||||||
| Rockwell Hardness, R Scale | D 785 | 110 | ||||||
| Izod Impact Strength, Notched @ 23°C (73°F) | D 256 | 842 J/m (15.8 ft·lbf/in.) | ||||||
| Impact Strength, Unnotched @ 23°C (73°F) | D 4812 | NB | ||||||
| Impact Resistance (Puncture), Energy @ Max. Load | ||||||||
| D 3763 | 62 J (46 ft·lbf) | ||||||
| D 3763 | 65 J (48 ft·lbf) | ||||||
| D 3763 | 67 J (49 ft·lbf) | ||||||
| Mechanical Properties (ISO Method) | ||||||||
| Tensile Strength @ Yield | ISO 527 | 45 MPa | ||||||
| Tensile Strength @ Break | ISO 527 | 51 MPa | ||||||
| Elongation @ Yield | ISO 527 | 7% | ||||||
| Elongation @ Break | ISO 527 | 142% | ||||||
| Tensile Modulus | ISO 527 | 1569 MPa | ||||||
| Flexural Modulus | ISO 178 | 1494 MPa | ||||||
| Flexural Strength | ISO 178 | 60 MPa | ||||||
| Izod Impact Strength, Notched | ||||||||
| ISO 180 | 78 kJ/m2 | ||||||
| ISO 180 | 12 kJ/m2 | ||||||
| Thermal Properties | ||||||||
| Deflection Temperature | ||||||||
| D 648 | 101°C (214°F ) | ||||||
| D 648 | 85°C (185°F ) | ||||||
| Optical Properties | ||||||||
| Total Transmittance | D 1003 | 91% | ||||||
| Haze | D 1003 | <1% | ||||||
| Typical Processing Conditions | ||||||||
| Drying Temperature | 88°C (190°F ) | |||||||
| Drying Time | 4-6 hrs | |||||||
| EBM Processing Melt Temperature | 235-255°C (455-490°F) | |||||||
| EBM Blow Mold Temperature | 15-50°C (60-122°F) | |||||||
| ISBM Processing Melt Temperature | 260-280°C (500-536°F) | |||||||
| ISBM Injection Mold Temperature | 40-65°C (104-149°F) | |||||||
| ISBM Blow Mold Temperature | 35-55°C (95-131°F) | |||||||