供应牙刷柄专用PCTG BR203 美国伊斯曼 透明牙刷柄用PCTG
深圳市百利丰塑胶原料有限公司
中国 东莞
产品属性
图文详情
品牌推荐
品牌/厂家
美国伊士曼
牌号
BR203
类型
正牌料
用途级别
注射级
产地
美国
熔体流动速率
10g/10min
密度
1.2g/cm3
拉伸强度
51kg/cm2
弯曲强度
65kg/cm2
弯曲模量
1850kg/cm2
缺口冲击强度
80kg.cm/cm
断裂伸长率
320%
成型收缩率
0.4%
热变形温度
73℃
脆化温度
-40℃
维卡软化点
NULL°F
Total Transmittance
91%
Regular Transmittance
89%
Haze
0.3%
干燥温度
70℃
干燥时间
3hrs
| Product Data Sheet Eastar™ Copolyester BR003, Natural | ||||||
| ||||||
| Product Description | ||||||
| Eastar™ BR003 Copolyester contains a mold release additive. It has excellent appearance and is nearly water-clear. Its most outstanding features are its chemical resistance and processing capabilities. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but BR003 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. BR003 is specifically formulated to provide the optimal combination of chemical resistance, bristle retention, strength, stiffness, processability, clarity, colorability, and feel for toothbrushes. Under existing United States Food and Drug Administration(FDA) regulations, Eastar™ BR003 copolyester may lawfully be used to make food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240. Migration tests on BR003 samples meet the compliance requirements of 21 CFR 177.1240(e)(1),(2) and (3). This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®. | ||||||
| Typical Properties | ||||||
| Propertya | Testb Method | Typical Value, Unitsc | ||||
| Specific Gravity | D 792 | 1.20 | ||||
| Mold Shrinkage Parallel to Flow, 3.2-mm (0.125-in.) thickness | D 955 | 0.002-0.006 mm/mm (0.002-0.006 in./in.) | ||||
| Mechanical Properties | ||||||
| Tensile Stress @ Yield | D 638 | 47 MPa (6900 psi) | ||||
| Tensile Stress @ Break | D 638 | 51 MPa (7400 psi) | ||||
| Elongation @ Yield | D 638 | 5% | ||||
| Elongation @ Break | D 638 | 320% | ||||
| Flexural Modulus | D 790 | 2000 MPa (2.9 x 105 psi ) | ||||
| Flexural Yield Strength | D 790 | 69 MPa (10000 psi) | ||||
| Rockwell Hardness, R Scale | D 785 | 103 | ||||
| Izod Impact Strength, Notched | ||||||
| D 256 | 80 J/m (1.5 ft·lbf/in.) | ||||
| D 256 | 40 J/m (0.7 ft·lbf/in.) | ||||
| Impact Strength, Unnotched | ||||||
| D 4812 | NB | ||||
| D 4812 | NB | ||||
| Impact Resistance (Puncture), Energy @ Max. Load | ||||||
| D 3763 | 42 J (31 ft·lbf) | ||||
| D 3763 | 48 J (35 ft·lbf) | ||||
| Mechanical Properties (ISO Method) | ||||||
| Tensile Strength @ Yield | ISO 527 | 47 MPa | ||||
| Tensile Strength @ Break | ISO 527 | 46 MPa | ||||
| Elongation @ Yield | ISO 527 | 4% | ||||
| Elongation @ Break | ISO 527 | 200% | ||||
| Tensile Modulus | ISO 527 | 1800 MPa | ||||
| Flexural Modulus | ISO 178 | 1850 MPa | ||||
| Flexural Strength | ISO 178 | 65 MPa | ||||
| Izod Impact Strength, Notched | ||||||
| ISO 180 | 7.8 kJ/m2 | ||||
| ISO 180 | 4.8 kJ/m2 | ||||
| Thermal Properties | ||||||
| Deflection Temperature | ||||||
| D 648 | 73°C (164°F) | ||||
| D 648 | 65°C (149°F) | ||||
| Optical Properties | ||||||
| Haze | D 1003 | 0.3% | ||||
| Regular Transmittance | D 1003 | 89% | ||||
| Total Transmittance | D 1003 | 91% | ||||
| Typical Processing Conditions | ||||||
| Drying Temperature | 70°C (160°F) | |||||
| Drying Time | 3 hrs | |||||
| Processing Melt Temperature | 230-280°C (450-530°F) | |||||
| Mold Temperature | 15-30°C (60-80°F) | |||||