KratonSEBS 美国科腾 1650MU
KRATON G1650 M
Styrene Ethylene Butylene Styrene Block Copolymer
Kraton Polymers LLC
产品说明：
Kraton G1650 M is a clear, linear triblock copolymer based on styrene and ethylene/butylene with a polystyrene content of 30%. It is supplied from North America in the physical form identified below.
- Kraton G1650 MU - supplied as a powder
Kraton G1650 M is used in compound formulations and as a modifier of thermoplastics. It may also find use in formulating adhesives, sealants, coatings and modified bitumens.物性信息：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 比重 | 0.910 | g/cm³ | ASTM D4025 |
| 表观密度 | 0.22 | g/cm³ | |
| 熔流率（熔体流动速率） (230°C/5.0 kg) | < 1.0 | g/10 min | ASTM D1238 |
| Antioxidant Additive 1 | 0.030 到 0.10 | % | 内部方法 |
| Polystyrene Content | 29 到 32 | % | 内部方法 |
| Total Extractables | | % | 内部方法 |
| 挥发物 | | % | 内部方法 |
| 溶液粘度 - Toluene, 25%wt (25°C) | 1.1 到 1.9 | Pa·s | 内部方法 |
| 补充信息 | 额定值 | | |
|---|
| Styrene/Rubber ratio | 30/70 | | |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|
| 肖氏硬度 (邵氏 A, 10 秒) | 72 | | ASTM D2240 |
| 弹性体 | 额定值 | 单位制 | 测试方法 |
|---|
| 拉伸应力 (300%应变) | 5.52 | MPa | ASTM D412 |
| 抗张强度 (屈服) | 34.5 | MPa | ASTM D412 |
| 伸长率 (断裂) | 500 | % | ASTM D412 |
SEBS加工
SEBS共混物可以采用注射、挤出及吹塑等热塑性加工制造各种物件。SEBS与SBS在产品结构方面有所不同，在加工温度也略有不同。在加工温度方面，SBS加工温度一般在150~200℃之间，而SEBS一般在190~260℃之间；SBS加工时，要求剪切速率较低，而SEBS加工时要求剪切速率较高；注塑成型时，SBS一般采用适中的剪切速率，挤出成型一般采用低压缩比的螺杆，而SEBS加工时，宜采用高注塑率和高压缩比的螺杆。
SEBS用途
1.SEBS具有较好的紫外线稳定性、抗氧性和热稳定性，所以在屋顶和修路用沥青中也可以使用。
2.SEBS与石蜡之间有比较好的相溶性，因此可用作纸制品较柔韧表面涂层。
3.SEBS在加热时没有明显的剪切流动时温度不敏感，因此它可以作为IPN的模板。（IPN的基本原理：两种不相溶的聚合物，可达到缠结链段的相互贯穿，如此就可以通过共价键交联将两种不相溶聚合物"锁定"在一起。）
4.SEBS油共混物的有机溶液可替代天然胶乳制造外科手套等制品，由于SEBS不含不饱和双键且纯度较高，在此且有以下两种优点：(1)抗氧性、抗臭氧性较好；(2)天然橡胶中含有蛋白质，会使某些病人产生危险的过敏反应，而这个共混物就不会。