Product data sheet产品数据表         H系特级(压实型)

     This product is a highly pure white compacted talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, high whiteness, good dispersity, excellent abrasion resistance and scratch resistance, easy to feed, good thermal stability and able to reduce the amount of other additives, it is suitable for filler of modified PA and reinforcement of high-end polymers. Due to the compacted form, higher compounding throughput that can be achieved, it can be used as a nucleant in semi-crystalline polymers.
       此产品是高纯度的压缩白滑石粉。由于其超薄度、超细度和均匀的粒径分布，白度高，分散性好，耐磨，耐刮擦，易喂料，热稳定性好，能降低其余助剂的添加量，很适合用于PA改性方面的填充和高端高分子聚合物的增强剂，由于其压实的形态、更高的复合量，也可作为半晶状的高分子聚合物的成核剂。

Compacted form 压实形态
Compacted bulk density压实体积密度:                                       M.I. 93003                          0.50 g/cm3
Loose bulk density松散体积密度:                                               M.I. 93003                          0.11 g/cm3
Moisture content at 105 °C 在105 °C时的水份含量:                     ISO 787/2 - M.I. 93005                 0.2%
Brightness by Minolta CR300白度(运用美能达CR300色度仪)
Y                                                                                                                                           96.0
L*   (CIE)                                                                                                                                98.5
a*   (CIE)                                                                                                                                 0.2

b*   (CIE)                                                                                                                                 0.5

Particle Size Distribution by Sedigraph      by Laser Mastersizer

沉降图粒径分布                                             激光粒度分析仪粒径分布

Sedimentation analysis沉降分析,                                           Laser diffraction激光衍射, 

Stokes’ Law斯托克定律 (ISO 13317-3)                                  Mie Theory米氏散射理论 (ISO 13320-1)
Median Diameter中值粒径-D50: 1.2 (1.2)*µm  D95: 3.6µm       Median Diameter中值粒径- D50: 3.9 (5)*µm   D95: 8.0µm



Physical Properties 物理特性
Density密度                                                                       DIN 53193                                2.8 g/cm3
Specific Surface B.E.T.总比表面积                                         DIN 66131/2                               11 m2/g
Hardness硬度                                                                     Mohs scale莫氏硬度值                             1
Chemical Analyses 化学分析 
SiO2二氧化硅                                                                                                                      61.5%
MgO氧化镁                                                                                                                         31.5%
CaO氧化钙                                                                                                                           0.2%
Fe2O3 三氧化二铁                                                                                                                0.2%
Al2O3 三氧化二铝                                                                                                                 0.2%
Loss on Ignition at 1050°C.在1050°C时的烧失量                                                                        6.0%