Product data sheet产品数据表      2000目透明级

       This product is a highly pure transparent talc. Due to its uniform particle size distribution, good dispersity, high whiteness, easily dispersed, good scratch resistance property, high hardness, excellent compatibility, high transparency and excellent transparency, it is suitable for reinforcement of polymers, it is recommended for filling of transparent polymers.
       此产品是高纯度透明滑石粉。由于其均匀的粒径分布，分散性好，白度高，易分散，耐刮擦，高硬度，良好的相容性，高透明性，透明度好，很适合做高分子聚合物的增强剂，推荐作为透明聚合物产品的填充。

Uncompacted form 未压实形态
Loose bulk density松散体积密度:                                               M.I. 93003                          0.20 g/cm3
Moisture content at 105 °C 在105 °C时的水份含量:                     ISO 787/2 - M.I. 93005                 0.2%
Brightness by Minolta CR300白度(运用美能达CR300色度仪)
Y                                                                                                                                           96.0
L*   (CIE)                                                                                                                                98.2
a*   (CIE)                                                                                                                                  0.2

b*   (CIE)                                                                                                                                  0.5

Particle Size Distribution by Sedigraph      by Laser Mastersizer

沉降图粒径分布                                               激光粒度分析仪粒径分布

Sedimentation analysis沉降分析,                                          Laser diffraction激光衍射, 

Stokes’ Law斯托克定律 (ISO 13317-3)                                  Mie Theory米氏散射理论 (ISO 13320-1)
Median Diameter中值粒径-D50: 3.0 (3)*µm  D95: 6.5µm         Median Diameter中值粒径- D50: 5.9 (6)*µm   D95:14.8µm



Physical Properties 物理特性
Density密度                                                                       DIN 53193                             2.8 g/cm3
Specific Surface B.E.T.总比表面积                                         DIN 66131/2                              6 m2/g
Hardness硬度                                                                     Mohs scale莫氏硬度值                          1
Chemical Analyses 化学分析
SiO2二氧化硅                                                                                                                    62.0%
MgO氧化镁                                                                                                                       31.5%
CaO氧化钙                                                                                                                         0.2%
Fe2O3 三氧化二铁                                                                                                               0.2%
Al2O3 三氧化二铝                                                                                                                0.2%
Loss on Ignition at 1050°C.在1050°C时的烧失量                                                                       5.0%