Product data sheet产品数据表         3000目

       This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, good dispersity, more platy, excellent improved stiffness/impact balance of products, unique performance, low shrinkage rate, stable dimension, it is suitable for reinforcement of polymers, it is recommended for polypropylene automotive exterior parts, interior parts, bumpers and dashboard products of high-end auto.
       此产品是高纯度的白滑石粉。由于其超薄度、超细度和均匀的粒径分布，分散性好，更多的片状，能很好的提高产品刚性和韧性（抗冲击性）的平衡，独特的性能，低收缩率，尺寸稳定，很适合做高分子聚合物的增强剂，推荐作为高端汽车聚丙烯外装品和内装品、保险杠和仪表盘等产品的材料。

Uncompacted form 未压实形态
Loose bulk density松散体积密度:                                               M.I. 93003                          0.20 g/cm3
Moisture content at 105 °C 在105 °C时的水份含量:                     ISO 787/2 - M.I. 93005                 0.2%
Brightness by Minolta CR300白度(运用美能达CR300色度仪)
Y                                                                                                                                           92.0
L*   (CIE)                                                                                                                                95.2
a*   (CIE)                                                                                                                                  0.2

b*   (CIE)                                                                                                                                  0.5

Particle Size Distribution by Sedigraph      by Laser Mastersizer

沉降图粒径分布                                               激光粒度分析仪粒径分布

Sedimentation analysis沉降分析,                                          Laser diffraction激光衍射, 

Stokes’ Law斯托克定律 (ISO 13317-3)                                  Mie Theory米氏散射理论 (ISO 13320-1)
Median Diameter中值粒径-D50: 3.0 (3)*µm  D95: 6.5µm         Median Diameter中值粒径- D50: 5.9 (6)*µm   D95:14.8µm



Physical Properties 物理特性
Density密度                                                                       DIN 53193                             2.8 g/cm3
Specific Surface B.E.T.总比表面积                                         DIN 66131/2                              6 m2/g
Hardness硬度                                                                     Mohs scale莫氏硬度值                          1
Chemical Analyses 化学分析
SiO2二氧化硅                                                                                                                    60.5%
MgO氧化镁                                                                                                                       31.5%
CaO氧化钙                                                                                                                         0.2%
Fe2O3 三氧化二铁                                                                                                               0.2%
Al2O3 三氧化二铝                                                                                                                0.2%
Loss on Ignition at 1050°C.在1050°C时的烧失量                                                                       7.0%