Product data sheet产品数据表       8000目

      This product is a highly pure white talc. Due to its high lamellarity, extreme fineness, uniform particle size distribution, good dispersity, more platy, excellent improved stiffness/impact balance of products, unique performance, low shrinkage rate, excellent scratch resistance property, it is suitable for reinforcement of high-end polymers and nucleant in semi-crystalline polymers, it is recommended for EPDM+ PP, PBT, PET products.
       此产品是高纯度的白滑石粉。由于其超薄度、超细度和均匀的粒径分布，分散性好，更多的片状，能很好的提高产品刚性和韧性（抗冲击性）的平衡，独特的性能，低收缩率，耐刮擦性能好，很适合做高端高分子聚合物的增强剂，也可作为半晶状的高分子聚合物的成核剂，推荐用于EPDM+PP，PBT，PET产品。

Uncompacted form 未压实形态
Loose bulk density松散体积密度:                                              M.I. 93003                          0.11 g/cm3
Moisture content at 105 °C 在105 °C时的水份含量:                     ISO 787/2 - M.I. 93005                 0.2%
Brightness by Minolta CR300白度(运用美能达CR300色度仪)
Y                                                                                                                                           96.0
L*   (CIE)                                                                                                                                98.5
a*   (CIE)                                                                                                                                  0.2

b*   (CIE)                                                                                                                                  0.5

Particle Size Distribution by Sedigraph                 by Laser Mastersizer

沉降图粒径分布                                                           激光粒度分析仪粒径分布

Sedimentation analysis沉降分析,                                          Laser diffraction激光衍射, 

Stokes’ Law斯托克定律 (ISO 13317-3)                                  Mie Theory米氏散射理论 (ISO 13320-1)
Median Diameter中值粒径-D50: 0.75 (1.0)*µm  D95: 2.5µm    Median Diameter中值粒径- D50: 3.5 (5)*µm  D95:7.0µm 



Physical Properties 物理特性
Density密度                                                                       DIN 53193                             2.8 g/cm3
Specific Surface B.E.T.总比表面积                                         DIN 66131/2                            11 m2/g
Hardness硬度                                                                     Mohs scale莫氏硬度值                          1
Chemical Analyses 化学分析
SiO2二氧化硅                                                                                                                    60.5%
MgO氧化镁                                                                                                                       31.5%
CaO氧化钙                                                                                                                         0.2%
Fe2O3 三氧化二铁                                                                                                               0.2%
Al2O3 三氧化二铝                                                                                                                0.2%
Loss on Ignition at 1050°C.在1050°C时的烧失量                                                                       7.0%